Antistatic Grip Fabric

ITEM TEST METHOD
Composition Polyester Filament yarn with carbon 
compound filament yarn		 ASTM-D-629
Weave 2/1 twill, 5mm grid
Weight 95 g/m2
Width 60 inch
Density warp 150 ends / inch
waft 109 ends / inch
Yarn Type warp Polyester 75 denier/36F ; Conductive 70 denier/25F
waft Polyester 75 denier/72F ; Conductive 70 denier/25F
Surface Resistivity 105~106 ohm/unit DIN 54345
Friction Charges Electrication Potential 35 V JIS L1094-B
Decay Time + - 0.01 sec NFPA-99
Air Permeability 6.0 c.c/cm2/sec JIS L1096-A
Tear Strength warp 3.0 Kg ISO 5082:1982-1"
waft 1.9 Kg grab test
Tensile Strength warp 58.0 Kg ISO 9290:1990-Falling"
waft 49.6 Kg Pendulum method B
Color Retention After water washing 4-5 grade ISO 105 C03-30min
After wet friction 4-5 grade ISO 105 D01:1993
Light fastness 4-5 grade ISO 105 E01:1994
After dry friction 4-5 grade ISO 105 B02:1994
Half-Life 4 sec JIS L1094-A
Application recommended for clean room garment (class 1000), hoods, caps, sock, masks, shoes

 
Antistatic Stripe Fabric

ITEM TEST METHOD
Composition Polyester Filament yarn with carbon 
compound filament yarn		 ASTM-D-629
Weave 2/1 twill, 5mm grid
Weight 95 g/m2
Width 60 inch
Density warp 150 ends / inch
waft 109 ends / inch
Yarn Type warp Polyester 75 denier/36F ; Conductive 70 denier/25F
waft Polyester 75 denier/72F ; Conductive 70 denier/25F
Surface Resistivity 105~106 ohm/unit DIN 54345
Friction Charges Electrication Potential 180 V JIS L1094-B
Decay Time + - 0.01 sec NFPA-99
Air Permeability 6.4 c.c/cm2/sec JIS L1096-A
Tear Strength warp 2.8 Kg ISO 5082:1982-1"
waft 1.7 Kg grab test
Tensile Strength warp 57.8 Kg ISO 9290:1990-Falling"
waft 52.7 Kg Pendulum method B
Color Retention After water washing 4-5 grade ISO 105 C03-30min
After wet friction 4-5 grade ISO 105 D01:1993
Light fastness 4-5 grade ISO 105 E01:1994
After dry friction 4-5 grade ISO 105 B02:1994
Half-Life 5 sec JIS L1094-A
Application recommended for clean room garment (class 1000), hoods, caps, sock, masks, shoes

 
SPECIFICATION

DIVISION

 BRAND

KOREA
UNIT HI# PUFC-N PUFRC-N PUFM60" PUFR60" PUFRC-BW PUFRC-BN PUFR60"B
MATERIAL  

POLYESTER 100%
STRUCTURE   3/2 TWILL 3/2 TWILL 2/1 TWILL 3/2 TWILL 2/1 TWILL 2/1 TWILL 2/1 TWILL 2/1 TWILL
FILTRATION (0.3-0.5 m) % 100 90 85 90 70 70 85 70
MOISTURE PERMEABILITY gr/m.24hr 7600 8000 85000 8000 8000 8000 8500 8000
AIR PERMEABILITY cc/cm.sec 0.5 1.8-2.1 3 1.0-2.2 8 11 3 8
STATIC CHARGEABILITY Volt 100 100 100 100 100 50 50 50
SURFACE RESISTANCE   10E8-9 10E8-9 10E8-9 10E8-9 10E8-9 10E5-7 10E5-7 10E5-7
TENSIL STRENGTH(WARP/WEFT) kg 50/50 50/50 50/50 50/50 50/50 50/50 50/50 50/50
CLASS UNIT   1 1-10 10-100 10-100 100-1000 1000 10-100 100-1000

38, 38/1 Orada Factory Land, Moo 4, Lumluka Road, T. Lumluka, A. Lumluka, Phatumthani 12150
Call Center: 0-2987-0882 Fax:0—2987-0223 E-Mail: marketingteam@pj-garment.com